Unevenly distributed thermal treatment of wood: preliminary study-density profiles
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F62156489%3A43110%2F16%3A43909713" target="_blank" >RIV/62156489:43110/16:43909713 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1007/s00107-016-1031-4" target="_blank" >http://dx.doi.org/10.1007/s00107-016-1031-4</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1007/s00107-016-1031-4" target="_blank" >10.1007/s00107-016-1031-4</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Unevenly distributed thermal treatment of wood: preliminary study-density profiles
Popis výsledku v původním jazyce
The present study aims to produce material with unevenly distributed density over cross section using thermal treatment. Beech (Fagus sylvatica L.) wood in dimensions of 65 x 65 x 700 mm(3) (R x T x L) was studied. Thermal modification at 160, 200 and 230 A degrees C was applied for different time exposure and evaluated using mass loss. Then, density profiles were measured in order to analyze density distribution over cross section. Low temperature and short process duration (15, 30, 60 and 120 min) with mass loss between 0.15 and 1.1 % were considered to be insufficient, whereas higher temperature of 200 and 230 A degrees C with average mass loss of 3.9 and 10 %, respectively, provides evenly modified cross section. However, uneven density profile was found for treatments at 230 A degrees C and ten 15 min intervals of exposure. Material with thermally modified surfaces with improved properties but unchanged mechanical behaviour in the middle section would provide another solution for applications for building purposes.
Název v anglickém jazyce
Unevenly distributed thermal treatment of wood: preliminary study-density profiles
Popis výsledku anglicky
The present study aims to produce material with unevenly distributed density over cross section using thermal treatment. Beech (Fagus sylvatica L.) wood in dimensions of 65 x 65 x 700 mm(3) (R x T x L) was studied. Thermal modification at 160, 200 and 230 A degrees C was applied for different time exposure and evaluated using mass loss. Then, density profiles were measured in order to analyze density distribution over cross section. Low temperature and short process duration (15, 30, 60 and 120 min) with mass loss between 0.15 and 1.1 % were considered to be insufficient, whereas higher temperature of 200 and 230 A degrees C with average mass loss of 3.9 and 10 %, respectively, provides evenly modified cross section. However, uneven density profile was found for treatments at 230 A degrees C and ten 15 min intervals of exposure. Material with thermally modified surfaces with improved properties but unchanged mechanical behaviour in the middle section would provide another solution for applications for building purposes.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JJ - Ostatní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/EE2.3.30.0031" target="_blank" >EE2.3.30.0031: Postdoktorské pozice v technických a ekonomických oborech na MENDELU</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
European Journal of Wood and Wood Products
ISSN
0018-3768
e-ISSN
—
Svazek periodika
74
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
3
Strana od-do
629-631
Kód UT WoS článku
000377363500017
EID výsledku v databázi Scopus
2-s2.0-84961218964