Anticorrosive protection of defected zinc coated layer, depending on the environment

Popis výsledku v původním jazyce

Zinc coating is one of the basic ways of anticorrosive protection. The aim of this article is to expose an artificially defected zinc coat to corrosion causes. Just two kinds of corrosion environment were chosen for this test. The first part of specimenswas exposed to an aggressive environment of salty fog and the other one was placed into a condensation chamber. There were used four kinds of specimens with the thickness of the zinc coat layer of 50, 60, 70, and 80 micrometr. Cracks of 5 and 10 micrometr were made on a bending pin. Such specimens were given into a condensation and salt-spray cabinet. The result is researching anticorrosive protection of defected and undamaged zinc coat layer in both environments.

Název v anglickém jazyce

Anticorrosive protection of defected zinc coated layer, depending on the environment

Popis výsledku anglicky

Zinc coating is one of the basic ways of anticorrosive protection. The aim of this article is to expose an artificially defected zinc coat to corrosion causes. Just two kinds of corrosion environment were chosen for this test. The first part of specimenswas exposed to an aggressive environment of salty fog and the other one was placed into a condensation chamber. There were used four kinds of specimens with the thickness of the zinc coat layer of 50, 60, 70, and 80 micrometr. Cracks of 5 and 10 micrometr were made on a bending pin. Such specimens were given into a condensation and salt-spray cabinet. The result is researching anticorrosive protection of defected and undamaged zinc coat layer in both environments.

Druh

D - Stať ve sborníku

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings International scientific conference" Material science and manufacturing technology"

ISBN

978-80-213-1792-5

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

Česká zemědělská univerzita v Praze

Místo vydání

Praha

Místo konání akce

Praha

Datum konání akce

26. 6. 2008

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—