Determination of grain size and resistance to corrosion of stainless steel welded pipes

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F62156489%3A43210%2F17%3A43911040" target="_blank" >RIV/62156489:43210/17:43911040 - isvavai.cz</a>

Výsledek na webu

<a href="https://acta.mendelu.cz/media/pdf/actaun_2017065010025.pdf" target="_blank" >https://acta.mendelu.cz/media/pdf/actaun_2017065010025.pdf</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.11118/actaun201765010025" target="_blank" >10.11118/actaun201765010025</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Determination of grain size and resistance to corrosion of stainless steel welded pipes

Popis výsledku v původním jazyce

Discover problems of welds is not so easy from time to time. Specially, If welding was made in rough environmental conditions such as high temperature, humidity and dusty wind. It is necessary to provide good conditions to realize basic step of welding. For welding, have been used welding procedures specification and procedure qualification record. However, dificult conditions, documentations rightness or human errors are always here. Common weld defects like cracks, porosity, lack of penetration and distortion can compromise the strength of the base metal, as well as the integrity of the weld. According of site inspection, there were suspicion of intercrystalline corrosion, inclusions, leaker or segregation in root of weld, root weld stretches to the pipe inside, the welded pipes are not in axially level, the not proper surface treatment after welding and keep the intervals between single welds to not overheat the pipes.

Název v anglickém jazyce

Determination of grain size and resistance to corrosion of stainless steel welded pipes

Popis výsledku anglicky

Discover problems of welds is not so easy from time to time. Specially, If welding was made in rough environmental conditions such as high temperature, humidity and dusty wind. It is necessary to provide good conditions to realize basic step of welding. For welding, have been used welding procedures specification and procedure qualification record. However, dificult conditions, documentations rightness or human errors are always here. Common weld defects like cracks, porosity, lack of penetration and distortion can compromise the strength of the base metal, as well as the integrity of the weld. According of site inspection, there were suspicion of intercrystalline corrosion, inclusions, leaker or segregation in root of weld, root weld stretches to the pipe inside, the welded pipes are not in axially level, the not proper surface treatment after welding and keep the intervals between single welds to not overheat the pipes.

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

20306 - Audio engineering, reliability analysis

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Universitatis Agriculturae et Silviculturae Mendelianae Brunensis

ISSN

1211-8516

e-ISSN

—

Svazek periodika

65

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

9

Strana od-do

25-33

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-85015864677