Degradation of the Layer Applied by Cold Kinetic Deposition

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F62156489%3A43210%2F21%3A43920888" target="_blank" >RIV/62156489:43210/21:43920888 - isvavai.cz</a>
Výsledek na webu
<a href="https://doi.org/10.1149/10501.0339ecst" target="_blank" >https://doi.org/10.1149/10501.0339ecst</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1149/10501.0339ecst" target="_blank" >10.1149/10501.0339ecst</a>

Jazyk výsledku
angličtina
Název v původním jazyce
Degradation of the Layer Applied by Cold Kinetic Deposition
Popis výsledku v původním jazyce
During the described experiment, a sample with a copper coating was formed on an aluminum substrate by cold spray. Subsequently, this sample was split for corrosion tests, where the split samples were exposed to a corrosive environment for different exposure times. The extent of corrosion degradation of the samples was evaluated by acoustic emission and metallographic analysis for corrosion-loaded samples for 100, 200 and 300 hours.
Název v anglickém jazyce
Degradation of the Layer Applied by Cold Kinetic Deposition
Popis výsledku anglicky
During the described experiment, a sample with a copper coating was formed on an aluminum substrate by cold spray. Subsequently, this sample was split for corrosion tests, where the split samples were exposed to a corrosive environment for different exposure times. The extent of corrosion degradation of the samples was evaluated by acoustic emission and metallographic analysis for corrosion-loaded samples for 100, 200 and 300 hours.

Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění
2021
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)