The physico-chemical structure and activity of hydrodesulphurizationcatalysts aged by accelerated method
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F62243136%3A_____%2F15%3AMPO06CL" target="_blank" >RIV/62243136:_____/15:MPO06CL - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/62243136:_____/15:MSM04CL
Výsledek na webu
<a href="http://www.sciencedirect.com/science/article/pii/S0920586115000085" target="_blank" >http://www.sciencedirect.com/science/article/pii/S0920586115000085</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.cattod.2014.12.040" target="_blank" >10.1016/j.cattod.2014.12.040</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The physico-chemical structure and activity of hydrodesulphurizationcatalysts aged by accelerated method
Popis výsledku v původním jazyce
The research was focused on the verification of the accelerated testing method for the testing of long term catalytic activity. The verification was carried out with two types (CoMo/Al2O3 and NiW/Al2O3) of commercial HDS catalysts. The catalysts were also placed into the industrial reactor and allowed to run for approximately 16 months under the industrial conditions. Then the residual activity of the catalysts was determined. The results from the accelerated and the industrial deactivation were compared. The accelerated method included (i) the testing of the initial activity and (ii) the determination of decreasing rate of activity. The deactivation step was implemented by the injection of highly aromatic raw materials with a coking tendency. After the deactivation period the typical conditions were set (pressure 4.5 MPa, hydrogen flow 300 Nm3/m3, and WHSV 1.0 kg/dm3cat). Subsequently, the reaction temperature for sulfur level 10 ppmw was determined. The implementation of accelerated
Název v anglickém jazyce
The physico-chemical structure and activity of hydrodesulphurizationcatalysts aged by accelerated method
Popis výsledku anglicky
The research was focused on the verification of the accelerated testing method for the testing of long term catalytic activity. The verification was carried out with two types (CoMo/Al2O3 and NiW/Al2O3) of commercial HDS catalysts. The catalysts were also placed into the industrial reactor and allowed to run for approximately 16 months under the industrial conditions. Then the residual activity of the catalysts was determined. The results from the accelerated and the industrial deactivation were compared. The accelerated method included (i) the testing of the initial activity and (ii) the determination of decreasing rate of activity. The deactivation step was implemented by the injection of highly aromatic raw materials with a coking tendency. After the deactivation period the typical conditions were set (pressure 4.5 MPa, hydrogen flow 300 Nm3/m3, and WHSV 1.0 kg/dm3cat). Subsequently, the reaction temperature for sulfur level 10 ppmw was determined. The implementation of accelerated
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CI - Průmyslová chemie a chemické inženýrství
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Catalysis Today
ISSN
0920-5861
e-ISSN
—
Svazek periodika
256
Číslo periodika v rámci svazku
2
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
8
Strana od-do
261-268
Kód UT WoS článku
000360657000006
EID výsledku v databázi Scopus
—