Catalytic Decomposition of Nitrous Oxide over Calcined Hydrotalcite-like Compounds.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F67985858%3A_____%2F02%3A27020223" target="_blank" >RIV/67985858:_____/02:27020223 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27360/02:00006940

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Catalytic Decomposition of Nitrous Oxide over Calcined Hydrotalcite-like Compounds.

Popis výsledku v původním jazyce

Mixed oxide based catalysts prepared by the thermal decomposition of Hydrotalcite-like compounds were used in catalytic decomposition of nitrous oxide into nitrogen and oxygen. The catalytic reaction was performed in a fixed-bed reactor at 1000 ppm N2O inlet concentration in the temperature range 603 - 723 K. Ni and Co-containing catalysts showed high activity in nitrous oxide decomposition. A very poor activity was observed for Mg-Al mixed oxide catalyst. The prepared catalysts were characterized by the thermal analysis, powder X-ray diffraction, infrared spectroscopy, BET surface area measurement, temperature-programmed reduction and temperature-programmed desorption. The determined reaction rate constants of N2O decomposition were approximately proportional to the amount of reducible components and inversely proportional to the amount of strong basic centres of catalyst.

Název v anglickém jazyce

Catalytic Decomposition of Nitrous Oxide over Calcined Hydrotalcite-like Compounds.

Popis výsledku anglicky

Mixed oxide based catalysts prepared by the thermal decomposition of Hydrotalcite-like compounds were used in catalytic decomposition of nitrous oxide into nitrogen and oxygen. The catalytic reaction was performed in a fixed-bed reactor at 1000 ppm N2O inlet concentration in the temperature range 603 - 723 K. Ni and Co-containing catalysts showed high activity in nitrous oxide decomposition. A very poor activity was observed for Mg-Al mixed oxide catalyst. The prepared catalysts were characterized by the thermal analysis, powder X-ray diffraction, infrared spectroscopy, BET surface area measurement, temperature-programmed reduction and temperature-programmed desorption. The determined reaction rate constants of N2O decomposition were approximately proportional to the amount of reducible components and inversely proportional to the amount of strong basic centres of catalyst.

Druh

D - Stať ve sborníku

CEP obor

CI - Průmyslová chemie a chemické inženýrství

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F02%2F0523" target="_blank" >GA106/02/0523: Vliv chemického a fázového složení materiálu na bázi hydrotalcitu na aktivitu katalyzátoru pro rozklad oxidu dusného</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2002

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Summaries.

ISBN

80-86059-33-2

ISSN

—

e-ISSN

—

Počet stran výsledku

1

Strana od-do

356

Název nakladatele

Process Engineering Publisher

Místo vydání

Prague

Místo konání akce

Prague [CZ]

Datum konání akce

25. 8. 2002

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—