Preparation and Properties of Pt-Mo Sulfide System Supported on Mesoporous Silica-Alumina

Popis výsledku v původním jazyce

The preparation and properties of Mo and Pt-Mo systems (14 wt.% Mo, ? 0.5 wt.% Pt) on a mesoporous silica-alumina (MSA) were studied. The Mo catalysts were characterized by X-Ray diffraction, N2 adsorption-desorption and transmission electron microscopy(TEM). The sulfided catalysts were tested in the simultaneous HDS of thiophene and HDN of pyridine. Deposition of ammonium heptamolybdate on MSA followed by sulfidation at 400oC for 4 h gave a well dispersed MoS2 phase, as confirmed by TEM. The additionof about 0.5 % Pt to the sulfided Mo(S)/MSA led to the significant improvements of HDS and HDN activities. Pt(acac)2 was more efficient Pt precursor than H2PtCl6 and Pt(NH3)4Cl2. The temperature of the sulfidation and the composition of the sulfiding gasduring activation of the Pt promoted catalyst had only smaller influence on activity.

Název v anglickém jazyce

Preparation and Properties of Pt-Mo Sulfide System Supported on Mesoporous Silica-Alumina

Popis výsledku anglicky

The preparation and properties of Mo and Pt-Mo systems (14 wt.% Mo, ? 0.5 wt.% Pt) on a mesoporous silica-alumina (MSA) were studied. The Mo catalysts were characterized by X-Ray diffraction, N2 adsorption-desorption and transmission electron microscopy(TEM). The sulfided catalysts were tested in the simultaneous HDS of thiophene and HDN of pyridine. Deposition of ammonium heptamolybdate on MSA followed by sulfidation at 400oC for 4 h gave a well dispersed MoS2 phase, as confirmed by TEM. The additionof about 0.5 % Pt to the sulfided Mo(S)/MSA led to the significant improvements of HDS and HDN activities. Pt(acac)2 was more efficient Pt precursor than H2PtCl6 and Pt(NH3)4Cl2. The temperature of the sulfidation and the composition of the sulfiding gasduring activation of the Pt promoted catalyst had only smaller influence on activity.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CI - Průmyslová chemie a chemické inženýrství

OECD FORD obor

—

Projekt

<a href="/cs/project/GA104%2F06%2F0870" target="_blank" >GA104/06/0870: Průzkum faktorů ovlivňujících aktivitu a selektivitu nanesených bimetalických sulfidů přechodových kovů v HDS a HDN reakcích</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Studies in Surface Science and Catalysis

ISSN

0167-2991

e-ISSN

—

Svazek periodika

162

Číslo periodika v rámci svazku

-

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

8

Strana od-do

489-496

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—