Designing (Al-)SBA-15 Catalyst Pellet with Unique Properties
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F67985858%3A_____%2F09%3A00356437" target="_blank" >RIV/67985858:_____/09:00356437 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Designing (Al-)SBA-15 Catalyst Pellet with Unique Properties
Popis výsledku v původním jazyce
Self-supporting pellets were successfully formed from SBA-15 and Al-SBA-15 powder without the addition of binder or plasticizer. Prepared self-supporting pellets maintained the porous structure of original powder. In comparison with parent sample, a decrease of mesopore surface area and mesopore volume up to 40 % was noticed in the case of pellets formed with the highest 17.7 MPa pressure. The Al-SBA-15 pellets prepared using 4.7 MPa forming pressure were enough mechanically stable to retain the structural integrity during batch alkylation of toluene with benzyl alcohol at 110 °C. The conversion reached with Al-SBA-15 pellets after 60 min of the reaction was about five times lower than that accomplished with powder Al-SBA-15.
Název v anglickém jazyce
Designing (Al-)SBA-15 Catalyst Pellet with Unique Properties
Popis výsledku anglicky
Self-supporting pellets were successfully formed from SBA-15 and Al-SBA-15 powder without the addition of binder or plasticizer. Prepared self-supporting pellets maintained the porous structure of original powder. In comparison with parent sample, a decrease of mesopore surface area and mesopore volume up to 40 % was noticed in the case of pellets formed with the highest 17.7 MPa pressure. The Al-SBA-15 pellets prepared using 4.7 MPa forming pressure were enough mechanically stable to retain the structural integrity during batch alkylation of toluene with benzyl alcohol at 110 °C. The conversion reached with Al-SBA-15 pellets after 60 min of the reaction was about five times lower than that accomplished with powder Al-SBA-15.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
CA - Anorganická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Characterisation of Porous Solids VIII
ISBN
978-1-84755-904-3
ISSN
—
e-ISSN
—
Počet stran výsledku
8
Strana od-do
—
Název nakladatele
Royal Society of Chemistry Publishing
Místo vydání
Cambridge
Místo konání akce
Edinburg
Datum konání akce
10. 6. 2008
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000269656900038