TiO2 Nanotubes Supported NiW Hydrodesulphurization Catalysts: Characterization and Activity
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F67985858%3A_____%2F13%3A00398837" target="_blank" >RIV/67985858:_____/13:00398837 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.apsusc.2012.11.001" target="_blank" >http://dx.doi.org/10.1016/j.apsusc.2012.11.001</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.apsusc.2012.11.001" target="_blank" >10.1016/j.apsusc.2012.11.001</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
TiO2 Nanotubes Supported NiW Hydrodesulphurization Catalysts: Characterization and Activity
Popis výsledku v původním jazyce
High surface area TiO2 nanotubes synthesized by alkali hydrothermal method, alumina and titania were used as a support for NiW hydrodesulphurization catalyst. Nickel salt of 12-tungstophosphoric acid (Ni3/2PW12O40) was applied as oxide precursor of the active components. A polytungstate phase evidenced by Raman spectroscopy was observed indicating the destruction of the initial heteropolyanion. Two times higher thiophene conversion was revealed on NiW catalyst supported on TiO2 nanotubes than those of catalysts supported on alumina and titania. Increased HDS activity of the NiW catalyst supported on TiO2 nanotubes could be related to both a higher amount of W oxysulfide entities in interaction with Ni2+ species observed with XPS analysis and to beneficial effect of titania nanotubes.
Název v anglickém jazyce
TiO2 Nanotubes Supported NiW Hydrodesulphurization Catalysts: Characterization and Activity
Popis výsledku anglicky
High surface area TiO2 nanotubes synthesized by alkali hydrothermal method, alumina and titania were used as a support for NiW hydrodesulphurization catalyst. Nickel salt of 12-tungstophosphoric acid (Ni3/2PW12O40) was applied as oxide precursor of the active components. A polytungstate phase evidenced by Raman spectroscopy was observed indicating the destruction of the initial heteropolyanion. Two times higher thiophene conversion was revealed on NiW catalyst supported on TiO2 nanotubes than those of catalysts supported on alumina and titania. Increased HDS activity of the NiW catalyst supported on TiO2 nanotubes could be related to both a higher amount of W oxysulfide entities in interaction with Ni2+ species observed with XPS analysis and to beneficial effect of titania nanotubes.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CI - Průmyslová chemie a chemické inženýrství
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Applied Surface Science
ISSN
0169-4332
e-ISSN
—
Svazek periodika
265
Číslo periodika v rámci svazku
JAN 15
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
5
Strana od-do
309-313
Kód UT WoS článku
000312958500048
EID výsledku v databázi Scopus
—