Effect of the Talc Filler on Structural, Water Vapor Barrier and Mechanical Properties of Poly(lactic acid) Composites.
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F67985858%3A_____%2F16%3A00467149" target="_blank" >RIV/67985858:_____/16:00467149 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1515/polyeng-2015-0014" target="_blank" >http://dx.doi.org/10.1515/polyeng-2015-0014</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1515/polyeng-2015-0014" target="_blank" >10.1515/polyeng-2015-0014</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of the Talc Filler on Structural, Water Vapor Barrier and Mechanical Properties of Poly(lactic acid) Composites.
Popis výsledku v původním jazyce
Poly(lactic acid) (PLA) based composite films with different content of talc (5-15 wt%) were prepared by the solvent casting method. The effect of talc on morphological, structural, thermal, barrier and mechanical properties of neat PLA was investigated. The PLA/talc composites revealed a polymorphic crystalline structure, as demonstrated by X-ray diffraction (XRD) study and differential scanning calorimetry (DSC) analysis. The PLA/talc composites also exhibited significantly improved barrier properties (up to 55% compared to neat PLA), as shown by water vapor permeability (WVP) tests. The puncture measurements showed improved mechanical properties at lower content of talc (up to 5 wt%), and increased brittleness of the PLA/talc composite films at higher talc concentrations.
Název v anglickém jazyce
Effect of the Talc Filler on Structural, Water Vapor Barrier and Mechanical Properties of Poly(lactic acid) Composites.
Popis výsledku anglicky
Poly(lactic acid) (PLA) based composite films with different content of talc (5-15 wt%) were prepared by the solvent casting method. The effect of talc on morphological, structural, thermal, barrier and mechanical properties of neat PLA was investigated. The PLA/talc composites revealed a polymorphic crystalline structure, as demonstrated by X-ray diffraction (XRD) study and differential scanning calorimetry (DSC) analysis. The PLA/talc composites also exhibited significantly improved barrier properties (up to 55% compared to neat PLA), as shown by water vapor permeability (WVP) tests. The puncture measurements showed improved mechanical properties at lower content of talc (up to 5 wt%), and increased brittleness of the PLA/talc composite films at higher talc concentrations.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CF - Fyzikální chemie a teoretická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Polymer Engineering
ISSN
0334-6447
e-ISSN
—
Svazek periodika
36
Číslo periodika v rámci svazku
2
Stát vydavatele periodika
DE - Spolková republika Německo
Počet stran výsledku
8
Strana od-do
181-188
Kód UT WoS článku
000371179800009
EID výsledku v databázi Scopus
2-s2.0-84960955057