On the electrospinning of PVB solutions

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F67985874%3A_____%2F10%3A00348878" target="_blank" >RIV/67985874:_____/10:00348878 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

On the electrospinning of PVB solutions

Popis výsledku v původním jazyce

Extension rheological characteristics belong to the principal description of polymer jet formation during a process of electrospinning. However, in spite of nearly absence of shear deformation of polymer solutions during the process of their spinnability, it seems that shear electrorheological characteristics can serve as an indicator of good or bad quality of an electrospun template. The experiments were carried out with four polyvinylbutyral (PVB) solutions in concentration of 10 wt%. Shear viscosities in absence (?0) and presence (?) of electric field were measured using a rotational rheometer equipped with an electrorheological cell. It was shown that the good solvents of PVB exhibit an almost constant curve of ?/?0 vs. electric field strength, whereas the viscosity curves for the poor solvents exhibit enhancement. This enhancement corresponds to better quality of electrospun templates (obtained for polymer solutions of PVB with poor solvents).

Název v anglickém jazyce

On the electrospinning of PVB solutions

Popis výsledku anglicky

Extension rheological characteristics belong to the principal description of polymer jet formation during a process of electrospinning. However, in spite of nearly absence of shear deformation of polymer solutions during the process of their spinnability, it seems that shear electrorheological characteristics can serve as an indicator of good or bad quality of an electrospun template. The experiments were carried out with four polyvinylbutyral (PVB) solutions in concentration of 10 wt%. Shear viscosities in absence (?0) and presence (?) of electric field were measured using a rotational rheometer equipped with an electrorheological cell. It was shown that the good solvents of PVB exhibit an almost constant curve of ?/?0 vs. electric field strength, whereas the viscosity curves for the poor solvents exhibit enhancement. This enhancement corresponds to better quality of electrospun templates (obtained for polymer solutions of PVB with poor solvents).

Druh

D - Stať ve sborníku

CEP obor

BK - Mechanika tekutin

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA200600703" target="_blank" >IAA200600703: Výzkum tokového chování nové třídy metalocenových polymerů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Conference Proceedings

ISBN

978-80-87294-19-2

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

—

Název nakladatele

TANGER

Místo vydání

Ostrava

Místo konání akce

Olomouc

Datum konání akce

12. 10. 2010

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—