Compositional trends in low-temperature photoluminescence of heavily Er-doped GeS(2)-Ga(2)S(3) glasses

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F67985882%3A_____%2F11%3A00367920" target="_blank" >RIV/67985882:_____/11:00367920 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.jnoncrysol.2010.11.075" target="_blank" >http://dx.doi.org/10.1016/j.jnoncrysol.2010.11.075</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jnoncrysol.2010.11.075" target="_blank" >10.1016/j.jnoncrysol.2010.11.075</a>

Jazyk výsledku
angličtina
Název v původním jazyce
Compositional trends in low-temperature photoluminescence of heavily Er-doped GeS(2)-Ga(2)S(3) glasses
Popis výsledku v původním jazyce
The influence of temperature and glass composition on the photoluminescence (PL) efficiency of Er3+ ions embedded in (GeS2)100x(Ga2S3)x (x=20, 25 and 33 mol%) glasses has been studied. The typical 4f?4f emission bands of Er3+ ions at around 830, 1000 and1550 nm have been observed in the whole investigated temperature range from 300 K down to 10 K for all the compositions. New 4f?4f luminescence bands, in excess of the three basic ones, have been observed at 670, 870, 1120, 1260 and 1350 nm for x=25.
Název v anglickém jazyce
Compositional trends in low-temperature photoluminescence of heavily Er-doped GeS(2)-Ga(2)S(3) glasses
Popis výsledku anglicky
The influence of temperature and glass composition on the photoluminescence (PL) efficiency of Er3+ ions embedded in (GeS2)100x(Ga2S3)x (x=20, 25 and 33 mol%) glasses has been studied. The typical 4f?4f emission bands of Er3+ ions at around 830, 1000 and1550 nm have been observed in the whole investigated temperature range from 300 K down to 10 K for all the compositions. New 4f?4f luminescence bands, in excess of the three basic ones, have been observed at 670, 870, 1120, 1260 and 1350 nm for x=25.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—

Projekt
<a href="/cs/project/GA104%2F08%2F0734" target="_blank" >GA104/08/0734: Speciální skelné materiály pro fotonické aplikace</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)