Preparation and Properties of Er-Doped ZrO2 Nanocrystalline Phase-Separated Preforms of Optical Fibers by MCVD Process

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F67985882%3A_____%2F12%3A00387436" target="_blank" >RIV/67985882:_____/12:00387436 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Preparation and Properties of Er-Doped ZrO2 Nanocrystalline Phase-Separated Preforms of Optical Fibers by MCVD Process

Popis výsledku v původním jazyce

The fabrication of Er-doped ZrO2-based nanocrystalline phase-separated silica optical preforms by the modified chemical vapor deposition process and solution-doping techniques is presented. Fabricated preform cores are nearly transparent and contain phase-separated rare-earth-doped nanocrystalline particles with diameters mainly in a range from 20 to 80 similar to nm. High concentrations of erbium and aluminum in preform cores of about 0.3 and 14 similar to mol%, respectively, have been achieved withoutdefects on the corecladding interface. Spectral losses in a range 800-1600 similar to nm and fluorescence spectra of erbium ions around 1550 similar to nm measured on a fiber drawn from the preform are reported.

Název v anglickém jazyce

Preparation and Properties of Er-Doped ZrO2 Nanocrystalline Phase-Separated Preforms of Optical Fibers by MCVD Process

Popis výsledku anglicky

The fabrication of Er-doped ZrO2-based nanocrystalline phase-separated silica optical preforms by the modified chemical vapor deposition process and solution-doping techniques is presented. Fabricated preform cores are nearly transparent and contain phase-separated rare-earth-doped nanocrystalline particles with diameters mainly in a range from 20 to 80 similar to nm. High concentrations of erbium and aluminum in preform cores of about 0.3 and 14 similar to mol%, respectively, have been achieved withoutdefects on the corecladding interface. Spectral losses in a range 800-1600 similar to nm and fluorescence spectra of erbium ions around 1550 similar to nm measured on a fiber drawn from the preform are reported.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JA - Elektronika a optoelektronika, elektrotechnika

OECD FORD obor

—

Projekt

<a href="/cs/project/GPP102%2F10%2FP554" target="_blank" >GPP102/10/P554: Erbiem dopované nanokrystalické fázově separované křemenné materiály s vylepšenými spektrálními vlastnostmi</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

International Journal of Applied Ceramic Technology

ISSN

1546-542X

e-ISSN

—

Svazek periodika

9

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

8

Strana od-do

341-348

Kód UT WoS článku

000301229900012

EID výsledku v databázi Scopus

—