Oxidation behaviour and mechanical properties of carbon fibre composites with methylphenylsiloxane-based matrix and pyrolytic carbon coating.

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F67985891%3A_____%2F01%3A08010064" target="_blank" >RIV/67985891:_____/01:08010064 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Oxidation behaviour and mechanical properties of carbon fibre composites with methylphenylsiloxane-based matrix and pyrolytic carbon coating.
Popis výsledku v původním jazyce
Properties of carbon fibre composites pyrolysed in nitrogen at 600-1000.mult.C with Toray M46 fibres and matrix derived from poly-methylphenylsiloxane-based resin were investigated.The surface layer (pyrolytic carbon 3-11.mu.m) was effective in reducingthe weight loss and increasing the bending strength measured in vacuum at 600.mult.C.
Název v anglickém jazyce
Oxidation behaviour and mechanical properties of carbon fibre composites with methylphenylsiloxane-based matrix and pyrolytic carbon coating.
Popis výsledku anglicky
Properties of carbon fibre composites pyrolysed in nitrogen at 600-1000.mult.C with Toray M46 fibres and matrix derived from poly-methylphenylsiloxane-based resin were investigated.The surface layer (pyrolytic carbon 3-11.mu.m) was effective in reducingthe weight loss and increasing the bending strength measured in vacuum at 600.mult.C.

Projekt
<a href="/cs/project/ME%20163" target="_blank" >ME 163: Příprava uhlíkových materiálů se separační schopností</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění
2001
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)