Influence of T-stress on the rate of propagation of fatigue cracks.

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F00%3A07013123" target="_blank" >RIV/68081723:_____/00:07013123 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Influence of T-stress on the rate of propagation of fatigue cracks.
Popis výsledku v původním jazyce
Two-parameter fracture mechanics is used to the description of the rate of propagation of fatigue cracks. The aim is to elucidate the experimentally observed effect of the speciemn geometry on the rate of propagation of a fatigue crack. The different levels of constraint are quantified by means of the T-stress.
Název v anglickém jazyce
Influence of T-stress on the rate of propagation of fatigue cracks.
Popis výsledku anglicky
Two-parameter fracture mechanics is used to the description of the rate of propagation of fatigue cracks. The aim is to elucidate the experimentally observed effect of the speciemn geometry on the rate of propagation of a fatigue crack. The different levels of constraint are quantified by means of the T-stress.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—

Projekt
<a href="/cs/project/GA106%2F99%2F1173" target="_blank" >GA106/99/1173: Aplikace dvouparametrové lomové mechaniky na šíření únavových trhlin</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění
2000
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)