Microstructural aspects of phosphorus grain boundary segregation in low alloy steels.

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F01%3A07013119" target="_blank" >RIV/68081723:_____/01:07013119 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Microstructural aspects of phosphorus grain boundary segregation in low alloy steels.
Popis výsledku v původním jazyce
The influence of microstructure on phosphorus grain boundary segregation in 2.6Cr-1Mo-0.3V low alloy steel was investigated by Auger and transmission electron microscopy. It was found that the phosphorus grain boundary segregation during the aging of thesteel at 773 K is faster in as-tempered microstructure than in as-quenched material. The lower dislocation density and the indirectly evidenced lower carbon content in ferrite matrix were considered to accelerate the kinetics of phosphorus segregation.
Název v anglickém jazyce
Microstructural aspects of phosphorus grain boundary segregation in low alloy steels.
Popis výsledku anglicky
The influence of microstructure on phosphorus grain boundary segregation in 2.6Cr-1Mo-0.3V low alloy steel was investigated by Auger and transmission electron microscopy. It was found that the phosphorus grain boundary segregation during the aging of thesteel at 773 K is faster in as-tempered microstructure than in as-quenched material. The lower dislocation density and the indirectly evidenced lower carbon content in ferrite matrix were considered to accelerate the kinetics of phosphorus segregation.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály