On the mutual relation between thermodynamic interaction coefficients and the diffusion interaction coefficients.
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F01%3A07013139" target="_blank" >RIV/68081723:_____/01:07013139 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
On the mutual relation between thermodynamic interaction coefficients and the diffusion interaction coefficients.
Popis výsledku v původním jazyce
This contribution deals with the mutual relation of the thermodynamic interaction coefficients .epsilon. and the diffusion interaction coefficients .beta.. For the given welded joints of steels P2V and P3/V with the chemical composition in wt. : steel P2(0.48Mn, 2.20Cr, 1.29Ni, 0.59Mo, 95.44Fe (ba1)), steel P3 (0.98Mn, 18.33Cr, 9.35Ni, 71.34Fe (ba1)), steel V (0.66Mn, 0.09Cr, 0.05Ni, 0.004Mo, 2.34Si, 96.856Fe (ba1)), the thermodynamic interaction coefficients .epsilon. and the diffusion interaction coefficients .beta. were calculated. The calculation was carried out on the basis of the original measurements of carbon redistribution in the welded joints of steels P2/V and P3IV. The welded joints of steels were annealed in the temperature range of 500 to 750 C with a temperature step of 50 C. The thermodynamic interaction coefficients .epsilon. were determined from the concentration discontinuity of carbon at the interface of the given welded joints of steels, whereas the diffusion inte
Název v anglickém jazyce
On the mutual relation between thermodynamic interaction coefficients and the diffusion interaction coefficients.
Popis výsledku anglicky
This contribution deals with the mutual relation of the thermodynamic interaction coefficients .epsilon. and the diffusion interaction coefficients .beta.. For the given welded joints of steels P2V and P3/V with the chemical composition in wt. : steel P2(0.48Mn, 2.20Cr, 1.29Ni, 0.59Mo, 95.44Fe (ba1)), steel P3 (0.98Mn, 18.33Cr, 9.35Ni, 71.34Fe (ba1)), steel V (0.66Mn, 0.09Cr, 0.05Ni, 0.004Mo, 2.34Si, 96.856Fe (ba1)), the thermodynamic interaction coefficients .epsilon. and the diffusion interaction coefficients .beta. were calculated. The calculation was carried out on the basis of the original measurements of carbon redistribution in the welded joints of steels P2/V and P3IV. The welded joints of steels were annealed in the temperature range of 500 to 750 C with a temperature step of 50 C. The thermodynamic interaction coefficients .epsilon. were determined from the concentration discontinuity of carbon at the interface of the given welded joints of steels, whereas the diffusion inte
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2001
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Acta Metallurgica Slovaca
ISSN
1335-1532
e-ISSN
—
Svazek periodika
7
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
5
Strana od-do
61-65
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—