Microstructure of CMSX-4 single crystals after creep and fatigue.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F01%3A07013150" target="_blank" >RIV/68081723:_____/01:07013150 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Microstructure of CMSX-4 single crystals after creep and fatigue.

Popis výsledku v původním jazyce

Changes of microstructure of single crystals CMSX-4 in consequence of creep deformation were used for explanation of experimentally determined difference between creep behavior in tension and compression. Two characteristic cyclic deformation features were observed after fatigue loading on specimen surface, namely short lines along the traces of {001} planes and persistent slip bands as long lines along the traces of the active {111} slip planes. Conclusions concerning the slip activity were drawn fromthe comparison of the observed features with the cyclic stress-strain response of CMSX-4 alloy.

Název v anglickém jazyce

Microstructure of CMSX-4 single crystals after creep and fatigue.

Popis výsledku anglicky

Changes of microstructure of single crystals CMSX-4 in consequence of creep deformation were used for explanation of experimentally determined difference between creep behavior in tension and compression. Two characteristic cyclic deformation features were observed after fatigue loading on specimen surface, namely short lines along the traces of {001} planes and persistent slip bands as long lines along the traces of the active {111} slip planes. Conclusions concerning the slip activity were drawn fromthe comparison of the observed features with the cyclic stress-strain response of CMSX-4 alloy.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/IBS2041001" target="_blank" >IBS2041001: Degradace vlastností a životnost inženýrských materiálů při jejich mechanickém namáhání</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Metallurgica Slovaca

ISSN

1335-1532

e-ISSN

—

Svazek periodika

7

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

5

Strana od-do

409-413

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—