CALCULATION OF THE CRITICAL STRESS IN TWO-PHASE MATERIALS.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F01%3A07013199" target="_blank" >RIV/68081723:_____/01:07013199 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26110/01:PU23225

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

CALCULATION OF THE CRITICAL STRESS IN TWO-PHASE MATERIALS.

Popis výsledku v původním jazyce

One of the primary reasons for the observed deviation of the behaviour of concrete from predictions based on linear elastic fracture mechanics can be the interaction between a crack and a material inhomogenity such as a particle which necessarily existsin such a material. on this paper, concrete is modelled as a two-phase material and the behaviour of a crack with its tip on the interface between two different materials is studied. In contrast to cracks in homogeneous materials the stress singularity for a crack terminating at the interface is of the type r -.lambda. , where the value of the stress singularity exponent,. .lambda. , is in the interval 0 < .lambda. < 1. This means that classical fracture mechanics theory and criterion cannot be applied.In the paper a new stability criterion is formulated. Conditions for the stability of the crack terminating at the interface between two materials are then used to estimate the critical stress for the intersection of coarse aggregate par

Název v anglickém jazyce

CALCULATION OF THE CRITICAL STRESS IN TWO-PHASE MATERIALS.

Popis výsledku anglicky

One of the primary reasons for the observed deviation of the behaviour of concrete from predictions based on linear elastic fracture mechanics can be the interaction between a crack and a material inhomogenity such as a particle which necessarily existsin such a material. on this paper, concrete is modelled as a two-phase material and the behaviour of a crack with its tip on the interface between two different materials is studied. In contrast to cracks in homogeneous materials the stress singularity for a crack terminating at the interface is of the type r -.lambda. , where the value of the stress singularity exponent,. .lambda. , is in the interval 0 < .lambda. < 1. This means that classical fracture mechanics theory and criterion cannot be applied.In the paper a new stability criterion is formulated. Conditions for the stability of the crack terminating at the interface between two materials are then used to estimate the critical stress for the intersection of coarse aggregate par

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Structural Engineering, Mechanics and Computation.

ISBN

0-08-043948-9

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

737-744

Název nakladatele

ELSEVIER

Místo vydání

N/A

Místo konání akce

Cape Town [ZA]

Datum konání akce

2. 4. 2001

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—