Fatigue crack initiation in fcc crystals.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F01%3A07013213" target="_blank" >RIV/68081723:_____/01:07013213 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue crack initiation in fcc crystals.

Popis výsledku v původním jazyce

Initiation of fatigue cracks both in model fcc single crystals and in fcc single crystals used in engineering practice is discussed. The emphasis is placed on the role of different types of cyclic slip localisation. It is shown that the phenomenon of persistent slip bands (PSBs) is confined to single crystals of sufficiently high stacking fault energy cycled at a relatively narrow range of loading conditions. For single crystals of not suitable orientations and/or of low stacking fault energy cycled under stresses and/or strains outside the critical range and/or under high temperatures the cyclic plasticity manifests itself by other forms of slip activity leading to the formation of surface hill-valley topography.

Název v anglickém jazyce

Fatigue crack initiation in fcc crystals.

Popis výsledku anglicky

Initiation of fatigue cracks both in model fcc single crystals and in fcc single crystals used in engineering practice is discussed. The emphasis is placed on the role of different types of cyclic slip localisation. It is shown that the phenomenon of persistent slip bands (PSBs) is confined to single crystals of sufficiently high stacking fault energy cycled at a relatively narrow range of loading conditions. For single crystals of not suitable orientations and/or of low stacking fault energy cycled under stresses and/or strains outside the critical range and/or under high temperatures the cyclic plasticity manifests itself by other forms of slip activity leading to the formation of surface hill-valley topography.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA2041002" target="_blank" >IAA2041002: Mikrostrukturní aspekty vrubové citlivosti superslitinových monokrystalů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Materials Structure and Micromechanisms of Fracture.

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

9

Strana od-do

263-271

Název nakladatele

VUT

Místo vydání

Brno

Místo konání akce

Brno [CZ]

Datum konání akce

27. 6. 2001

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—