Two-Parameter Approach for Short Cracks at Notches.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F01%3A07013226" target="_blank" >RIV/68081723:_____/01:07013226 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Two-Parameter Approach for Short Cracks at Notches.

Popis výsledku v původním jazyce

A two parameter constraint-based fracture mechanics method is applied to the behavior of microstructurally and mechanically short fatigue cracks. A short crack in the vicinity of a grain boundary and a crack which is engulfed by the plastic strain fieldof a notch are studied as examples. The different levels of stress constraint are quantified by using the T-stress and the Q parameter. The corresponding calculations are performed by using a finite element method (ANSYS system). The influence of the T values on the propagation of short fatigue cracks is analyzed. The size of the plastic zone and the crack closure are significantly affected by the level of constraint. The influence of constraint on small fatigue crack growth kinetic is studied under theassumption that the controlling variable for the rate of propagation of the fatigue crack is the size of the plastic zone.

Název v anglickém jazyce

Two-Parameter Approach for Short Cracks at Notches.

Popis výsledku anglicky

A two parameter constraint-based fracture mechanics method is applied to the behavior of microstructurally and mechanically short fatigue cracks. A short crack in the vicinity of a grain boundary and a crack which is engulfed by the plastic strain fieldof a notch are studied as examples. The different levels of stress constraint are quantified by using the T-stress and the Q parameter. The corresponding calculations are performed by using a finite element method (ANSYS system). The influence of the T values on the propagation of short fatigue cracks is analyzed. The size of the plastic zone and the crack closure are significantly affected by the level of constraint. The influence of constraint on small fatigue crack growth kinetic is studied under theassumption that the controlling variable for the rate of propagation of the fatigue crack is the size of the plastic zone.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F99%2F1173" target="_blank" >GA106/99/1173: Aplikace dvouparametrové lomové mechaniky na šíření únavových trhlin</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

International Conference on Materials structure and Micromechanics of Fracture - MSMF-3.

ISBN

80-214-1892-3

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

"X1"-"X5"

Název nakladatele

Brno Univesity of Technology

Místo vydání

Brno

Místo konání akce

Brno [CZ]

Datum konání akce

27. 6. 2001

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—