Preparation and properties of Mg-Fe and Mg-Ni-Fe nanocomposites.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F01%3A07013270" target="_blank" >RIV/68081723:_____/01:07013270 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Preparation and properties of Mg-Fe and Mg-Ni-Fe nanocomposites.

Popis výsledku v původním jazyce

We prepared Mg-Fe and Mg-Fe-Ni nanocomposites using spark synthesis of pure Mg, and Fe or permalloy (Ni3Fe) electrodes. The magnetic separation and sedimentation treatments were used for separation of nanocrystaline parts from the as-prepared powders. Inthe Mg-Fe sample, a-Fe, Fe in Mg, and FeO phases were determined using the Mössbauer phase analysis, and Mg, MgO, and a-Fe by the x-ray diffraction measurements. The Fe in Mg phase with approx. 8at.% Fe is a new metastable phase not described in equilibrium phase diagram handbooks until now. Its temperature dependence of magnetization showed spin-glass like behaviour of the sample. An annealing in vacuum (10-3 Pa) or in the protective atmosphere (H2) caused transformation of the Fe in Mg phase into a-Fe. With increasing a-Fe content an increase of the FeO was observed. The Mg-Fe-Ni nanocomposite exhibits similar behaviour and phase composition but the Ni3Fe phase was replaced the a-Fe and different features of the Fe(Ni) in Mg phase we

Název v anglickém jazyce

Preparation and properties of Mg-Fe and Mg-Ni-Fe nanocomposites.

Popis výsledku anglicky

We prepared Mg-Fe and Mg-Fe-Ni nanocomposites using spark synthesis of pure Mg, and Fe or permalloy (Ni3Fe) electrodes. The magnetic separation and sedimentation treatments were used for separation of nanocrystaline parts from the as-prepared powders. Inthe Mg-Fe sample, a-Fe, Fe in Mg, and FeO phases were determined using the Mössbauer phase analysis, and Mg, MgO, and a-Fe by the x-ray diffraction measurements. The Fe in Mg phase with approx. 8at.% Fe is a new metastable phase not described in equilibrium phase diagram handbooks until now. Its temperature dependence of magnetization showed spin-glass like behaviour of the sample. An annealing in vacuum (10-3 Pa) or in the protective atmosphere (H2) caused transformation of the Fe in Mg phase into a-Fe. With increasing a-Fe content an increase of the FeO was observed. The Mg-Fe-Ni nanocomposite exhibits similar behaviour and phase composition but the Ni3Fe phase was replaced the a-Fe and different features of the Fe(Ni) in Mg phase we

Druh

D - Stať ve sborníku

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

11th Czech and Slovak Conference on Magnetism CSMAG'01 - Programme & Abstracts.

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

1

Strana od-do

55

Název nakladatele

Šafarik University Košice

Místo vydání

Košice

Místo konání akce

Košice [SK]

Datum konání akce

20. 8. 2001

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—