Fracture toughness transferability - from small to full scale specimens.
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F02%3A07023011" target="_blank" >RIV/68081723:_____/02:07023011 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fracture toughness transferability - from small to full scale specimens.
Popis výsledku v původním jazyce
The capability of pre-cracked Charpy type specimens for prediction of fracture toughness characteristics for standard (1T) specimens has been analysed. Two methodologies - the toughness scaling models and the master curve methodology have been followed.Cast,low-carbon manganese steel from midthickness of thick walled plate was used as experimental material being tested as a candidate material for container casks of spent nuclear fuel. The Dodds-Anderson toughness scaling model was applied for toughnessdata correction from PCVN pecimens. This approach was combined with master curve methodology for fracture oughness - temperature diagram and loading rate effects predictions. The Koppenhoefer scaling diagram based on Weibull stress was also tested supplying good correlation of predicted data with real behaviour.
Název v anglickém jazyce
Fracture toughness transferability - from small to full scale specimens.
Popis výsledku anglicky
The capability of pre-cracked Charpy type specimens for prediction of fracture toughness characteristics for standard (1T) specimens has been analysed. Two methodologies - the toughness scaling models and the master curve methodology have been followed.Cast,low-carbon manganese steel from midthickness of thick walled plate was used as experimental material being tested as a candidate material for container casks of spent nuclear fuel. The Dodds-Anderson toughness scaling model was applied for toughnessdata correction from PCVN pecimens. This approach was combined with master curve methodology for fracture oughness - temperature diagram and loading rate effects predictions. The Koppenhoefer scaling diagram based on Weibull stress was also tested supplying good correlation of predicted data with real behaviour.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/IAA2041003" target="_blank" >IAA2041003: Mikromechanika křehkého lomu a statistické modely</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2002
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
New Trends in Fatigue and Fracture.
ISBN
—
ISSN
—
e-ISSN
—
Počet stran výsledku
1
Strana od-do
"X1"-"X5"
Název nakladatele
LFM Université de Metz
Místo vydání
Metz
Místo konání akce
Metz [FR]
Datum konání akce
8. 4. 2002
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—