Micromechanical Aspects of Constraint Effect at Brittle Fracture Initiation.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F02%3A07023023" target="_blank" >RIV/68081723:_____/02:07023023 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Micromechanical Aspects of Constraint Effect at Brittle Fracture Initiation.

Popis výsledku v původním jazyce

Applying the two-parameter fracture mechanics approach to the analysis of failure initiation condition in three-point bend specimens with shallow and deep cracks were tested at various temperatures. Low carbon manganese cast steel was used for the analysis. The effect of crack length on the fracture toughness-temperature diagram has been analysed. Strong dependence of measured fracture toughness on crack tip constraint was observed, no evident differences in fracture morphology were identified except for quantitative ones. The effect of crack tip constraint on brittle fracture characteristics has been quantified by means of the Q-parameter. The role of cleavage fracture stress in brittle fracture initiation under the influence of crack tip constraint has been analysed.

Název v anglickém jazyce

Micromechanical Aspects of Constraint Effect at Brittle Fracture Initiation.

Popis výsledku anglicky

Applying the two-parameter fracture mechanics approach to the analysis of failure initiation condition in three-point bend specimens with shallow and deep cracks were tested at various temperatures. Low carbon manganese cast steel was used for the analysis. The effect of crack length on the fracture toughness-temperature diagram has been analysed. Strong dependence of measured fracture toughness on crack tip constraint was observed, no evident differences in fracture morphology were identified except for quantitative ones. The effect of crack tip constraint on brittle fracture characteristics has been quantified by means of the Q-parameter. The role of cleavage fracture stress in brittle fracture initiation under the influence of crack tip constraint has been analysed.

Druh

C - Kapitola v odborné knize

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2002

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název knihy nebo sborníku

Transferability of Fracture Mechanical Characteristics.

ISBN

—

Počet stran výsledku

14

Strana od-do

65-78

Počet stran knihy

—

Název nakladatele

Kluwer Academic Publishers

Místo vydání

Dordrecht

Kód UT WoS kapitoly

—