Cyclic plastic deformation and initiation of cracks in metals.
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F02%3A07023101" target="_blank" >RIV/68081723:_____/02:07023101 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Cyclic plastic deformation and initiation of cracks in metals.
Popis výsledku v původním jazyce
The initiation and early propagation of fatigue cracks are smoothly consequential processes without any clear border between them. At present there is no generally accepted quantitative description of the initiation process and the following propagationof the microstructurally small cracks. Thus, any numerical analysis of the initiation of cracks must be preceded by deeper understanding of physical mechanisms. The aim of the paper is to offer an overview of the present state of the art in the fatigue crack initiation in metals. The following items will be treated: (i) sites of crack initiation, (ii) prerequisites for crack initiation, (iii) mechanisms of crack initiation and (iv) end of initiation stage and beginning of the propagation stage.
Název v anglickém jazyce
Cyclic plastic deformation and initiation of cracks in metals.
Popis výsledku anglicky
The initiation and early propagation of fatigue cracks are smoothly consequential processes without any clear border between them. At present there is no generally accepted quantitative description of the initiation process and the following propagationof the microstructurally small cracks. Thus, any numerical analysis of the initiation of cracks must be preceded by deeper understanding of physical mechanisms. The aim of the paper is to offer an overview of the present state of the art in the fatigue crack initiation in metals. The following items will be treated: (i) sites of crack initiation, (ii) prerequisites for crack initiation, (iii) mechanisms of crack initiation and (iv) end of initiation stage and beginning of the propagation stage.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2002
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Fatigue 2002 /8./.
ISBN
—
ISSN
—
e-ISSN
—
Počet stran výsledku
16
Strana od-do
3491
Název nakladatele
Emas
Místo vydání
Cradley Heath
Místo konání akce
Stockholm [WB]
Datum konání akce
3. 6. 2002
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—