High temperature creep behaviour and microstructural changes of TAF 650 steel.

Popis výsledku v původním jazyce

The microstructure of W, Ni and Co containing high chromium martensitic steel TAF 650 was quantified by transmission electron microscopy and image analysis. Creep investigation of this steel reveals substantially longer time to fracture at lower stressesthan was expected from previous results. In order to find out microstructural features responsible for such improvement in the creep properties, microstructural investigations of TAF 650 steel after 18 700 hours creep exposure at temperature 650 C was performed. The results show that the synergetic effect of fine MX precipitates decreases due to Z-phase precipitation together with higher amount of Laves phase particles found in creep specimens compared to isothermally aged material is responsible for the creep strength. The prediction of creep behaviour based on a comparison of experimentally determined secondary phases and chemical composition with equilibrium values obtained by THERMO-Calc calculations are also provided.

Název v anglickém jazyce

High temperature creep behaviour and microstructural changes of TAF 650 steel.

Popis výsledku anglicky

The microstructure of W, Ni and Co containing high chromium martensitic steel TAF 650 was quantified by transmission electron microscopy and image analysis. Creep investigation of this steel reveals substantially longer time to fracture at lower stressesthan was expected from previous results. In order to find out microstructural features responsible for such improvement in the creep properties, microstructural investigations of TAF 650 steel after 18 700 hours creep exposure at temperature 650 C was performed. The results show that the synergetic effect of fine MX precipitates decreases due to Z-phase precipitation together with higher amount of Laves phase particles found in creep specimens compared to isothermally aged material is responsible for the creep strength. The prediction of creep behaviour based on a comparison of experimentally determined secondary phases and chemical composition with equilibrium values obtained by THERMO-Calc calculations are also provided.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2002

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Materials for Advanced Power Engineering 2002 /7./.

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

10

Strana od-do

1521-1530

Název nakladatele

Forschungszentrum Jülich GmbH, Central Library

Místo vydání

Jülich

Místo konání akce

Li&#232;ge [BE]

Datum konání akce

30. 9. 2002

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—