Interdiffusion in Pseudobinary Sections of Ni3Al-Co ternary system.
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F02%3A07023119" target="_blank" >RIV/68081723:_____/02:07023119 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Interdiffusion in Pseudobinary Sections of Ni3Al-Co ternary system.
Popis výsledku v původním jazyce
Interdiffusion in Ni(3)AI intermetallic alloyed by 0-19 at.% Co was studied in three pseudo-binary sections: C-Al= 22, c(co) = 3.5, and c(co) = 16 (c in at.%). The experiments were carried out at temperatures between 1173 and 1473 K. An attempt was madeto analyze the interdiffusion coefficient into intrinsic diffusivities of individual components. Since no detectable shift of tungsten inert markers was observed, it was concluded that the intrinsic diffusivities of element pairs with varying concentration (Al/Ni and Co/Ni) in respective pseudo-binary sections are approximately equal one to another. The interdiffusion in pseudo-binary alloys Al/Ni (c(co) = const.) runs slightly faster than that in pseudo-binary alloys Ni/Co (c(Al) = const.). The relations between the measured interdiffusion coefficients in the Ni3-xAlCox ordered gamma' phase agree well with literature data for the interdiffusion coefficients in both the ordered gamma' and gamma'+Co phases and also for the disordered Al-
Název v anglickém jazyce
Interdiffusion in Pseudobinary Sections of Ni3Al-Co ternary system.
Popis výsledku anglicky
Interdiffusion in Ni(3)AI intermetallic alloyed by 0-19 at.% Co was studied in three pseudo-binary sections: C-Al= 22, c(co) = 3.5, and c(co) = 16 (c in at.%). The experiments were carried out at temperatures between 1173 and 1473 K. An attempt was madeto analyze the interdiffusion coefficient into intrinsic diffusivities of individual components. Since no detectable shift of tungsten inert markers was observed, it was concluded that the intrinsic diffusivities of element pairs with varying concentration (Al/Ni and Co/Ni) in respective pseudo-binary sections are approximately equal one to another. The interdiffusion in pseudo-binary alloys Al/Ni (c(co) = const.) runs slightly faster than that in pseudo-binary alloys Ni/Co (c(Al) = const.). The relations between the measured interdiffusion coefficients in the Ni3-xAlCox ordered gamma' phase agree well with literature data for the interdiffusion coefficients in both the ordered gamma' and gamma'+Co phases and also for the disordered Al-
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F00%2F0173" target="_blank" >GA106/00/0173: Vzájemná difúze substitučních prvků v modifikovaných intermetalikách Ni3Al</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2002
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Intermetallics
ISSN
0966-9795
e-ISSN
—
Svazek periodika
10
Číslo periodika v rámci svazku
9
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
6
Strana od-do
859-864
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—