Preparation and properties of alpha-Fe and Fe3O4 nanocrystals in MgO and TiO2 Matrices
Popis výsledku v původním jazyce
Preparation of the nanocrystalline composites of iron and magnetite nanoparticles embedded in MgO or TiO2 matrices is described. The results of phase analysis obtained by means of Mössbauer spectroscopy, X-ray diffraction, TEM and magnetic measurements are reported. Coercive force of the samples of the composite formed by spherical Fe3O4 (mean size -20 nm) nanoparticles was 25?1 mT and for alpha-Fe (-30nm) it was 30?1 mT. These values were not influenced by the chemical difference of the matrix materials.
Název v anglickém jazyce
Preparation and properties of alpha-Fe and Fe3O4 nanocrystals in MgO and TiO2 Matrices
Popis výsledku anglicky
Preparation of the nanocrystalline composites of iron and magnetite nanoparticles embedded in MgO or TiO2 matrices is described. The results of phase analysis obtained by means of Mössbauer spectroscopy, X-ray diffraction, TEM and magnetic measurements are reported. Coercive force of the samples of the composite formed by spherical Fe3O4 (mean size -20 nm) nanoparticles was 25?1 mT and for alpha-Fe (-30nm) it was 30?1 mT. These values were not influenced by the chemical difference of the matrix materials.

Projekt
<a href="/cs/project/ME%20635" target="_blank" >ME 635: Fázová analýza nanokrystalických prášků pomocí rtg difrakce</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění
2004
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)