Nanocomposite material based on iron/graphite core-shell nanoparticles prepared by a two-step procedure

Popis výsledku v původním jazyce

We describe the phase composition and magnetic properties of the nanocomposite based on iron/graphite core-shell structured nanoparticles. This nanocomposite was prepared by a two-step procedure: in the first step, the original Fe-C-N based nanopowder was synthesized by the method of laser pyrolysis of gas phase reactants, and subsequently in the second step, it was heated up to 800°C in vacuum. Annealing in vacuum induced the formation and growth of iron/graphite core-shell structured nanoparticles. Both the originally synthesized Fe-C-N based nanopowder and the annealed nanopowder were characterized by TEM, XRD and magnetic measurements. The presence of iron nanoparticles with the mean diameter of 40 nm in the annealed state of the nanopowder was proved by XRD and TEM analysis. Mössbauer spectroscopy was used to observe a qualitative change in phase composition.

Název v anglickém jazyce

Nanocomposite material based on iron/graphite core-shell nanoparticles prepared by a two-step procedure

Popis výsledku anglicky

We describe the phase composition and magnetic properties of the nanocomposite based on iron/graphite core-shell structured nanoparticles. This nanocomposite was prepared by a two-step procedure: in the first step, the original Fe-C-N based nanopowder was synthesized by the method of laser pyrolysis of gas phase reactants, and subsequently in the second step, it was heated up to 800°C in vacuum. Annealing in vacuum induced the formation and growth of iron/graphite core-shell structured nanoparticles. Both the originally synthesized Fe-C-N based nanopowder and the annealed nanopowder were characterized by TEM, XRD and magnetic measurements. The presence of iron nanoparticles with the mean diameter of 40 nm in the annealed state of the nanopowder was proved by XRD and TEM analysis. Mössbauer spectroscopy was used to observe a qualitative change in phase composition.

Druh

D - Stať ve sborníku

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the International Conference NANO 04

ISBN

80-214-2793-0

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

288

Název nakladatele

VUTIUM Brno

Místo vydání

Praha

Místo konání akce

Brno

Datum konání akce

13. 10. 2004

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—