Creep behaviour of a magnesium alloy AS21 and its fibre-strengthened composite

Popis výsledku v původním jazyce

Compressive creep tests of a magnesium alloy and its fibre composite (with 27 vol.% of Saffil fibres) were performed in temperature interval from 423 to 523 K in order to judge the strengthening influence of fibres and to analyse possibilities of an explanation of physical bases of the creep strain. Both materials were prepared by squeeze casting. From stress and temperature dependence of the minimum creep rates, activation parameters of creep, i.e., the apparent activation energy and the stress sensitivity parameter of creep rate, were evaluated and compared with the purpose to suggest possible mechanisms of creep deformation. In both materials investigated, the stress sensitivity parameters and the activations energies are relatively high and cannotbe directly attributed to any creep mechanism. No threshold behaviour was observed in the stress dependence of the creep rates in both materials. A dependence of the creep behaviour on the orientation of composite specimens is presented.

Název v anglickém jazyce

Creep behaviour of a magnesium alloy AS21 and its fibre-strengthened composite

Popis výsledku anglicky

Compressive creep tests of a magnesium alloy and its fibre composite (with 27 vol.% of Saffil fibres) were performed in temperature interval from 423 to 523 K in order to judge the strengthening influence of fibres and to analyse possibilities of an explanation of physical bases of the creep strain. Both materials were prepared by squeeze casting. From stress and temperature dependence of the minimum creep rates, activation parameters of creep, i.e., the apparent activation energy and the stress sensitivity parameter of creep rate, were evaluated and compared with the purpose to suggest possible mechanisms of creep deformation. In both materials investigated, the stress sensitivity parameters and the activations energies are relatively high and cannotbe directly attributed to any creep mechanism. No threshold behaviour was observed in the stress dependence of the creep rates in both materials. A dependence of the creep behaviour on the orientation of composite specimens is presented.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F03%2F0843" target="_blank" >GA106/03/0843: Mikroprocesy plastické deformace v moderních slitinách a kompozitech na bázi lehkých kovů za zvýšených teplot</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Alloys and Compounds

ISSN

0925-8388

e-ISSN

—

Svazek periodika

378

Číslo periodika v rámci svazku

1-2

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

5

Strana od-do

167-171

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—