Confirmation of Low Stress Creep Regime in 9% Chromium Steel by Stress Change Creep Experiments

Popis výsledku v původním jazyce

High sensitive helicoid spring specimen creep technique was modified to allow stress changes during the low stress, low strain rate experiments. The results obtained on the P-91 type modified martensitic 9% Cr steel support the previous observations of the change of the creep deformation mechanism at low stresses. The stress exponent derived from the stress change experiments approaches a value of about 4.5, considerably higher than that derived from the constant stress experiments. On the other hand, it is much lower than the value of 12, reported for the power-law creep regime of the same steel at stresses above 100MPa. The creep behavior at low stresses is still not fully understood. The transient stages were observed after each stress change including back flow after the stress decrease. The relaxation periods are relatively long, notably after the stress decrease. The stress redistribution is suggested as a main source of the observed transient effects.

Název v anglickém jazyce

Confirmation of Low Stress Creep Regime in 9% Chromium Steel by Stress Change Creep Experiments

Popis výsledku anglicky

High sensitive helicoid spring specimen creep technique was modified to allow stress changes during the low stress, low strain rate experiments. The results obtained on the P-91 type modified martensitic 9% Cr steel support the previous observations of the change of the creep deformation mechanism at low stresses. The stress exponent derived from the stress change experiments approaches a value of about 4.5, considerably higher than that derived from the constant stress experiments. On the other hand, it is much lower than the value of 12, reported for the power-law creep regime of the same steel at stresses above 100MPa. The creep behavior at low stresses is still not fully understood. The transient stages were observed after each stress change including back flow after the stress decrease. The relaxation periods are relatively long, notably after the stress decrease. The stress redistribution is suggested as a main source of the observed transient effects.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Science and Engineering A

ISSN

0921-5093

e-ISSN

—

Svazek periodika

387-389

Číslo periodika v rámci svazku

-

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

6

Strana od-do

633-638

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—