Vliv středního napětí na růst krátkých únavových trhlin u nerezavějící oceli 316L

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F04%3A00108258" target="_blank" >RIV/68081723:_____/04:00108258 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of mean stress on short crack growth of fatigued 316L stainless steel

Popis výsledku v původním jazyce

Short crack growth mechanism and kinetics were studied in cylindrical specimens with a shallow notch in 316L steel cycled under constant plastic strain amplitude and constant mean stress. Cyclic creep strain, resulting from mean stress application, increases the density of slip markings in individual grains. Fatigue cracks initiated along strain localized areas and crack linking was the main mechanism of the early crack growth. Two different regimes were identified in short crack growth rate. In the first regime, initiated cracks grow with constant growth rate which is independent of the crack length. Later, the linear increase of the crack growth rate with the crack length can represent experimental data. The short crack growth rate in both regimes increases with increasing tensile mean stress

Název v anglickém jazyce

Effect of mean stress on short crack growth of fatigued 316L stainless steel

Popis výsledku anglicky

Short crack growth mechanism and kinetics were studied in cylindrical specimens with a shallow notch in 316L steel cycled under constant plastic strain amplitude and constant mean stress. Cyclic creep strain, resulting from mean stress application, increases the density of slip markings in individual grains. Fatigue cracks initiated along strain localized areas and crack linking was the main mechanism of the early crack growth. Two different regimes were identified in short crack growth rate. In the first regime, initiated cracks grow with constant growth rate which is independent of the crack length. Later, the linear increase of the crack growth rate with the crack length can represent experimental data. The short crack growth rate in both regimes increases with increasing tensile mean stress

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

The 15th European Conference of Fracture - Advanced Fracture Mechanics for Life and Safety Assessment

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

1

Strana od-do

1-2

Název nakladatele

Royal Institute of Technology

Místo vydání

Stockholm

Místo konání akce

Stockholm

Datum konání akce

11. 8. 2004

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—