Vztahy mezi mikrostrukturou a vlastnostmi ultrajemnozrnného hliníku připraveného metodou ECAP
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F04%3A00108275" target="_blank" >RIV/68081723:_____/04:00108275 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Microstructure/properties relationship in ultrafine grained aluminium processed by ECAP technique
Popis výsledku v původním jazyce
Extremely coarse grained aluminium (99.99 %) was subjected to severe plastic deformation (ECAP) at room temperature using the die that had a 90 angle between the die channels. Using this technique a bulk utlrafine grained material can be prepared. The properties of the ECAP material may considerably differ from properties of material with standard grain size. The microstructure of specimens processed by different number of ECAP passes (up to 12 passes), and after creep testing was examined using a scanning electron microscope (SEM) JEOL 6460 with EBSD ( Electron Backscatter Diffraction). The experimental results show that the banded microstructure of ultrafine grained aluminium after one pass by the ECAP die contains high amount of low angle boundaries( ~ 95 % ) and these are transformed into high angle boundaries by subsequent ECAP pressing. The microstructure after four passes contains more or less equiaxed grains, but the microstructure is still rather heterogenous. It is clear...
Název v anglickém jazyce
Microstructure/properties relationship in ultrafine grained aluminium processed by ECAP technique
Popis výsledku anglicky
Extremely coarse grained aluminium (99.99 %) was subjected to severe plastic deformation (ECAP) at room temperature using the die that had a 90 angle between the die channels. Using this technique a bulk utlrafine grained material can be prepared. The properties of the ECAP material may considerably differ from properties of material with standard grain size. The microstructure of specimens processed by different number of ECAP passes (up to 12 passes), and after creep testing was examined using a scanning electron microscope (SEM) JEOL 6460 with EBSD ( Electron Backscatter Diffraction). The experimental results show that the banded microstructure of ultrafine grained aluminium after one pass by the ECAP die contains high amount of low angle boundaries( ~ 95 % ) and these are transformed into high angle boundaries by subsequent ECAP pressing. The microstructure after four passes contains more or less equiaxed grains, but the microstructure is still rather heterogenous. It is clear...
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JJ - Ostatní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/IAA2041301" target="_blank" >IAA2041301: Creepové procesy v ultrajemných kovech a slitinách připravených technikou ECAP</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2004
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Junior-Euromat 2004
ISBN
—
ISSN
—
e-ISSN
—
Počet stran výsledku
1
Strana od-do
1
Název nakladatele
DGM
Místo vydání
Švýcarsko
Místo konání akce
Lausanne
Datum konání akce
6. 9. 2004
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—