Creep a mikrostruktura téměř stechiometrických slitin TiAl

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F04%3A00108281" target="_blank" >RIV/68081723:_____/04:00108281 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Creep and microstructure of near-gamma TiAl alloys

Popis výsledku v původním jazyce

Creep strength and microstructure of Ti-48Al-2Cr-2Nb-1B and Ti-46Al-2W-0.5Si-(0.7B) alloys are compared. The influence of a prior-to-creep heat treatment on the initial microstructure is investigated. The isothermally forged and heat treated Ti-48Al-2Cr-2Nb-1B alloy was tested in nearly lamellar and equiaxed modifications while the cast and HIP-ped Ti-46Al-2W-0.5Si alloy was either nearly lamellar or duplex before creep. All these microstructural variants were crept in tension at 1023 K and at differentapplied stresses. Experimental results obtained in the present study suggest that, in spite of creep strength variations resulting from the different microstructural states, the Ti-46Al-2W-0.5Si alloy performs better than the Ti-48Al-2Cr-2Nb-1B alloy. Transmission electron microscopy analysis provided evidence that W- and Si-rich phases that precipitate both, on the lamellar boundaries and inside the gamma grains, contribute to the superior creep strength of the Ti-46Al-2W-0.5Si alloy

Název v anglickém jazyce

Creep and microstructure of near-gamma TiAl alloys

Popis výsledku anglicky

Creep strength and microstructure of Ti-48Al-2Cr-2Nb-1B and Ti-46Al-2W-0.5Si-(0.7B) alloys are compared. The influence of a prior-to-creep heat treatment on the initial microstructure is investigated. The isothermally forged and heat treated Ti-48Al-2Cr-2Nb-1B alloy was tested in nearly lamellar and equiaxed modifications while the cast and HIP-ped Ti-46Al-2W-0.5Si alloy was either nearly lamellar or duplex before creep. All these microstructural variants were crept in tension at 1023 K and at differentapplied stresses. Experimental results obtained in the present study suggest that, in spite of creep strength variations resulting from the different microstructural states, the Ti-46Al-2W-0.5Si alloy performs better than the Ti-48Al-2Cr-2Nb-1B alloy. Transmission electron microscopy analysis provided evidence that W- and Si-rich phases that precipitate both, on the lamellar boundaries and inside the gamma grains, contribute to the superior creep strength of the Ti-46Al-2W-0.5Si alloy

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Intermetallics

ISSN

0966-9795

e-ISSN

—

Svazek periodika

12

Číslo periodika v rámci svazku

7-9

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

705-711

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—