Evolution of Microstructure During Creep in Gamma Ti-52Al at 1100 K and High Applied Stresses

Popis výsledku v původním jazyce

Microstructural changes due to compression creep in gamma Ti-52Al phase at 1100 K and 250 MPa have been investigated. The microstructures always consisted of three fundamental deformation modes: (i) ordinary dislocations, (ii) superdislocations and (iii)deformation twins that contributed to the overall creep strain from the very beginning of creep. This microstructural evolution and the corresponding metal-type creep behaviour contrasts with the sharp creep rate minima and a lack of superdislocations and deformation twins reported earlier for specimens deformed at 1100 K and applied stresses below 200 MPa. The partitioning of the total strain among fundamental deformation modes is estimated and the link between sharp minima of creep rate and the insufficient activation of c-component plastic displacements is suggested

Název v anglickém jazyce

Evolution of Microstructure During Creep in Gamma Ti-52Al at 1100 K and High Applied Stresses

Popis výsledku anglicky

Microstructural changes due to compression creep in gamma Ti-52Al phase at 1100 K and 250 MPa have been investigated. The microstructures always consisted of three fundamental deformation modes: (i) ordinary dislocations, (ii) superdislocations and (iii)deformation twins that contributed to the overall creep strain from the very beginning of creep. This microstructural evolution and the corresponding metal-type creep behaviour contrasts with the sharp creep rate minima and a lack of superdislocations and deformation twins reported earlier for specimens deformed at 1100 K and applied stresses below 200 MPa. The partitioning of the total strain among fundamental deformation modes is estimated and the link between sharp minima of creep rate and the insufficient activation of c-component plastic displacements is suggested

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Zeitschrift fuer Metallkunde

ISSN

0044-3093

e-ISSN

—

Svazek periodika

95

Číslo periodika v rámci svazku

11

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

9

Strana od-do

1011-1019

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—