Vliv povrchové karbonitridace plazmovou imerzní iontovou implantací na únavové chování austenitické nerezavějící oceli 316L

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F05%3A00026256" target="_blank" >RIV/68081723:_____/05:00026256 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of surface carbonitriding by plasma immersion ion implantation on the fatigue behaviour of 316L austenitic stainless stee

Popis výsledku v původním jazyce

Cylindrical specimens of 316L austenitic stainless steel in as-received condition and with surface carbonitriding by plasma immersion ion implantation were cyclically strained under plastic strain control. Micro-hardness depth profile of hardened surfacelayer was measured. Mössbauer spectroscopy and X-ray diffraction were used to study the phase composition of the treated layer. Stress-strain response and fatigue life data of both materials were obtained. Surface relief and fracture surface were examined to study fatigue damage mechanisms. Two domains separated by the transitional plastic strain amplitude could be distinguished in fatigue behaviour of the treated steel. In the low amplitude domain, the main crack originates in subsurface region resulting in the prolonged lifetime. The main crack initiates at the surface in the high amplitude domain and the fatigue life of the treated steel is reduced compared to the untreated one.

Název v anglickém jazyce

Effect of surface carbonitriding by plasma immersion ion implantation on the fatigue behaviour of 316L austenitic stainless stee

Popis výsledku anglicky

Cylindrical specimens of 316L austenitic stainless steel in as-received condition and with surface carbonitriding by plasma immersion ion implantation were cyclically strained under plastic strain control. Micro-hardness depth profile of hardened surfacelayer was measured. Mössbauer spectroscopy and X-ray diffraction were used to study the phase composition of the treated layer. Stress-strain response and fatigue life data of both materials were obtained. Surface relief and fracture surface were examined to study fatigue damage mechanisms. Two domains separated by the transitional plastic strain amplitude could be distinguished in fatigue behaviour of the treated steel. In the low amplitude domain, the main crack originates in subsurface region resulting in the prolonged lifetime. The main crack initiates at the surface in the high amplitude domain and the fatigue life of the treated steel is reduced compared to the untreated one.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Computer Methods and Experimental Measurements for Surface Effects and Contact Mechanics /7./

ISBN

1-84564-022-5

ISSN

—

e-ISSN

—

Počet stran výsledku

10

Strana od-do

13-22

Název nakladatele

WIT Press

Místo vydání

Southampton

Místo konání akce

Bologna

Datum konání akce

5. 9. 2005

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—