O společném účinku teploty a poloměru zaoblení kořene vrubu na lomovou houževnatost

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F05%3A00028304" target="_blank" >RIV/68081723:_____/05:00028304 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

To Joint of Temperature and Notch Root Radius on Fracture Toughness

Popis výsledku v původním jazyce

For low-alloyed cast ferritic steel simultaneous effect of temperature and notch root radius on fracture toughness has been investigated. Due to fact that fracture tests were performed on notched specimens (cylindrical tensile specimens with circumferential notch having three notch root radii), the concept of Notch Fracture Mechanics was applied. Volumetric fracture criterion with two parameters, effective stress and effective distance, was developed. The goal of the work was to quantify the influence of notch radius on transition temperature and notch fracture toughness, and, in addition, to present jointly the role of both these parameters in fracture behaviour.

Název v anglickém jazyce

To Joint of Temperature and Notch Root Radius on Fracture Toughness

Popis výsledku anglicky

For low-alloyed cast ferritic steel simultaneous effect of temperature and notch root radius on fracture toughness has been investigated. Due to fact that fracture tests were performed on notched specimens (cylindrical tensile specimens with circumferential notch having three notch root radii), the concept of Notch Fracture Mechanics was applied. Volumetric fracture criterion with two parameters, effective stress and effective distance, was developed. The goal of the work was to quantify the influence of notch radius on transition temperature and notch fracture toughness, and, in addition, to present jointly the role of both these parameters in fracture behaviour.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/IBS2041001" target="_blank" >IBS2041001: Degradace vlastností a životnost inženýrských materiálů při jejich mechanickém namáhání</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Engineering Mechanics = Inženýrská mechanika

ISSN

1210-2717

e-ISSN

—

Svazek periodika

12

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

12

Strana od-do

11-22

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—