Odhad prahových hodnot pro šíření trhliny přes rozhraní dvou materiálů beroucí v potaz existenci reziduálních napětí

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F06%3A00045097" target="_blank" >RIV/68081723:_____/06:00045097 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Estimation of the fatigue threshold values for a crack propagating through a bi-material interface taking into account residua stresses

Popis výsledku v původním jazyce

This article deals with the behaviour of a fatigue crack propagating across a bi-material interface. A stability criterion for the crack touching the bi-material interface, taking into account the residual stresses closing the crack faces, is formulated.Linear elastic fracture mechanics are assumed to apply and the finite-element method is used in the calculations. The criterion proposed is applied to determine the fatigue threshold stress for crack propagation across the interface. Two different geometries are considered. It is shown that the threshold values for crack propagation are influenced by the residual stresses closing the crack and by the specific combination of the elastic constants of the materials used. The results contribute to a betterunderstanding of the failure of structures with bi-material interfaces (protective layers, composite materials, etc.).

Název v anglickém jazyce

Estimation of the fatigue threshold values for a crack propagating through a bi-material interface taking into account residua stresses

Popis výsledku anglicky

This article deals with the behaviour of a fatigue crack propagating across a bi-material interface. A stability criterion for the crack touching the bi-material interface, taking into account the residual stresses closing the crack faces, is formulated.Linear elastic fracture mechanics are assumed to apply and the finite-element method is used in the calculations. The criterion proposed is applied to determine the fatigue threshold stress for crack propagation across the interface. Two different geometries are considered. It is shown that the threshold values for crack propagation are influenced by the residual stresses closing the crack and by the specific combination of the elastic constants of the materials used. The results contribute to a betterunderstanding of the failure of structures with bi-material interfaces (protective layers, composite materials, etc.).

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GP106%2F04%2FP084" target="_blank" >GP106/04/P084: Vliv rozhraní dvou materiálů na šíření únavových trhlin</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials and Technology

ISSN

1580-2949

e-ISSN

—

Svazek periodika

40

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

SI - Slovinská republika

Počet stran výsledku

4

Strana od-do

157-160

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—