-Fe nanočástice připravené rozkladem pentakarbonylu železa v mikrovlnném výboji

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F06%3A00045330" target="_blank" >RIV/68081723:_____/06:00045330 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

-Fe Nanoparticles Prepared by Microwave Plasma Decomposition of Iron Pentacarbonyl

Popis výsledku v původním jazyce

The nanocrystalline iron powder has been prepared by the introducing of Fe(CO)5 vapor into the microwave induced argon discharge. A microwave 2.45 GHz source was operated at 430 W. The reaction was performed in a quartz tube passing through the microwavewaveguide. The in-situ passivation using air was applied after synthesis. The powder was characterised by TEM, XRD, and Mössbauer spectroscopy. According to our TEM investigation, the produced passivated powder included aggregated core-shell nanoparticles. The cores consist of -Fe and the shell is supposed to be iron oxide (indicated by TEM). The presence of -Fe and iron oxides was confirmed by XRD and Mössbauer spectroscopy. The mean coherence domain size of -Fe cores was estimated to be 30 nm. The synthesized nanopowder exhibits ferromagnetic behaviour.

Název v anglickém jazyce

-Fe Nanoparticles Prepared by Microwave Plasma Decomposition of Iron Pentacarbonyl

Popis výsledku anglicky

The nanocrystalline iron powder has been prepared by the introducing of Fe(CO)5 vapor into the microwave induced argon discharge. A microwave 2.45 GHz source was operated at 430 W. The reaction was performed in a quartz tube passing through the microwavewaveguide. The in-situ passivation using air was applied after synthesis. The powder was characterised by TEM, XRD, and Mössbauer spectroscopy. According to our TEM investigation, the produced passivated powder included aggregated core-shell nanoparticles. The cores consist of -Fe and the shell is supposed to be iron oxide (indicated by TEM). The presence of -Fe and iron oxides was confirmed by XRD and Mössbauer spectroscopy. The mean coherence domain size of -Fe cores was estimated to be 30 nm. The synthesized nanopowder exhibits ferromagnetic behaviour.

Druh

D - Stať ve sborníku

CEP obor

BL - Fyzika plasmatu a výboje v plynech

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

NANO´05 International Conference Proceedings

ISBN

80-214-3085-0

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

366-369

Název nakladatele

Brno University of Technology, Faculty of Mechanical Engineering

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

8. 11. 2005

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—