Únavové chování lité niklové superslitiny Inconel 792-5A při 700 °C
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F06%3A00047239" target="_blank" >RIV/68081723:_____/06:00047239 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fatigue behaviour of cast nickel based superalloy inconel 792-5A at 700 °C
Popis výsledku v původním jazyce
Cylindrical specimens of cast polycrystalline superalloy Inconel 792-5A were cyclically strained under total strain control at 700 °C up to fracture. Cyclic hardening curves, cyclic stress-strain curve and fatigue life curve were documented. Dislocationstructure was studied with the technique of oriented foils in transmission electron microscope. Scanning electron microscopy was used to investigate the surface relief. High amplitude straining is characterized by initial hardening followed by the tendency to saturation. Low amplitude cycling results in the stabilized stress response. Surface slip markings and slip bands lying along {111} planes in the interior of grains cut both channels and precipitates. Experimental results concerning the surface relief and dislocation structure are used to discuss the stress-strain response.
Název v anglickém jazyce
Fatigue behaviour of cast nickel based superalloy inconel 792-5A at 700 °C
Popis výsledku anglicky
Cylindrical specimens of cast polycrystalline superalloy Inconel 792-5A were cyclically strained under total strain control at 700 °C up to fracture. Cyclic hardening curves, cyclic stress-strain curve and fatigue life curve were documented. Dislocationstructure was studied with the technique of oriented foils in transmission electron microscope. Scanning electron microscopy was used to investigate the surface relief. High amplitude straining is characterized by initial hardening followed by the tendency to saturation. Low amplitude cycling results in the stabilized stress response. Surface slip markings and slip bands lying along {111} planes in the interior of grains cut both channels and precipitates. Experimental results concerning the surface relief and dislocation structure are used to discuss the stress-strain response.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials and Technology
ISSN
1580-2949
e-ISSN
—
Svazek periodika
40
Číslo periodika v rámci svazku
5
Stát vydavatele periodika
SI - Slovinská republika
Počet stran výsledku
4
Strana od-do
175-178
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—