Dislocation arrangements in cyclically strained Inconel 713 LC

Popis výsledku v původním jazyce

Dislocation arrangement was studied in cast polycrystalline INCONEL 713LC superalloy cyclically strained to failure at 300K, 773K, 973K and 1073K temperatures.The characteristic dislocation substructures and their evolution in cyclic straining with different strain amplitudes up to fracture were documented.Three-dimensional dislocation arrangement in individual grains was determined using the technique of oriented foils in transmission electron microscope.Planar dislocation arrangements in the form of bands parallel to the {111} planes were observed in specimens cycled at all temperatures.These bands passing through both channels and precipitates are formed as ladder-like bands at room temperature and as thin slabs of high dislocation density at high temperatures.They represent the zones of cyclic plastic strain localization in the material. Surface observation revealed pronounced slip markings with extrusions and intrusions and crack initiation along slip markings at room temperature.

Název v anglickém jazyce

Dislocation arrangements in cyclically strained Inconel 713 LC

Popis výsledku anglicky

Dislocation arrangement was studied in cast polycrystalline INCONEL 713LC superalloy cyclically strained to failure at 300K, 773K, 973K and 1073K temperatures.The characteristic dislocation substructures and their evolution in cyclic straining with different strain amplitudes up to fracture were documented.Three-dimensional dislocation arrangement in individual grains was determined using the technique of oriented foils in transmission electron microscope.Planar dislocation arrangements in the form of bands parallel to the {111} planes were observed in specimens cycled at all temperatures.These bands passing through both channels and precipitates are formed as ladder-like bands at room temperature and as thin slabs of high dislocation density at high temperatures.They represent the zones of cyclic plastic strain localization in the material. Surface observation revealed pronounced slip markings with extrusions and intrusions and crack initiation along slip markings at room temperature.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Fracture of nano and engineering materials and structures

ISBN

1-4020-4971-4

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

1-8

Název nakladatele

Springer

Místo vydání

Dordrecht

Místo konání akce

Alexandroupolis

Datum konání akce

3. 7. 2006

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—