Elementární procesy martensitické transformace v Ni-bohatých monokrystalech NiTi s Ni4Ti3 precipitáty
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F06%3A00322623" target="_blank" >RIV/68081723:_____/06:00322623 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Elementary martensitic transformation processes in Ni-rich NiTi single crystals with Ni4Ti3 precipitates
Popis výsledku v původním jazyce
The present study shows that multiple step martensitic transformations can be observed in aged Ni-rich NiTi single crystals. Aging of solution annealed and water quenched Ni-rich NiTi single crystals results in a homogeneous precipitation of coherent Ni4Ti3 particles. When the interparticle spacing reaches a critical value (order of magnitude: 200 nm), three distinct transformation processes are observed on cooling from the high temperature phase using differential scanning calorimetry (DSC) and in-situtransmission electron microscopy (TEM). The transformation sequence begins with the formation of R-phase starting from all precipitate/matrix-interfaces (first step). The transformation continues with the formation of B19? near and its subsequent growthalong all precipitate/matrix-interfaces (second step). Finally, the matrix in between the precipitates transforms to B19? (third step).
Název v anglickém jazyce
Elementary martensitic transformation processes in Ni-rich NiTi single crystals with Ni4Ti3 precipitates
Popis výsledku anglicky
The present study shows that multiple step martensitic transformations can be observed in aged Ni-rich NiTi single crystals. Aging of solution annealed and water quenched Ni-rich NiTi single crystals results in a homogeneous precipitation of coherent Ni4Ti3 particles. When the interparticle spacing reaches a critical value (order of magnitude: 200 nm), three distinct transformation processes are observed on cooling from the high temperature phase using differential scanning calorimetry (DSC) and in-situtransmission electron microscopy (TEM). The transformation sequence begins with the formation of R-phase starting from all precipitate/matrix-interfaces (first step). The transformation continues with the formation of B19? near and its subsequent growthalong all precipitate/matrix-interfaces (second step). Finally, the matrix in between the precipitates transforms to B19? (third step).
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F05%2F0918" target="_blank" >GA106/05/0918: Vztah mezi přípravou, strukturou a transformačním chováním tvarově paměťových slitin NiTi</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Acta Materialia
ISSN
1359-6454
e-ISSN
—
Svazek periodika
54
Číslo periodika v rámci svazku
13
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
18
Strana od-do
—
Kód UT WoS článku
000239823800013
EID výsledku v databázi Scopus
—