Název v původním jazyce

Assessment of thermodynamic properties and phase diagram in the Ag?In?Pd system

Popis výsledku v původním jazyce

Phase equilibria in the Ag?In?Pd system were determined at 500 °C based on experimental results for 16 alloys. A ternary intermetallic compound (T1) in the palladium-rich region was confirmed by X-ray diffractometry. The experimental data were first compared with the results of a CALPHAD-type prediction, based on binary thermodynamic data using only a symmetrical Redlich?Kister?Muggianu model. In a second step, the thermodynamic modeling of the different phases in this ternary system was refined by including ternary interactions, and the phase diagram was calculated for the temperature range between 500 and 700 °C. With the optimized thermodynamic parameters the phase diagram was extrapolated to 200 °C and compared with preliminary experimental results.

Název v anglickém jazyce

Assessment of thermodynamic properties and phase diagram in the Ag?In?Pd system

Popis výsledku anglicky

Phase equilibria in the Ag?In?Pd system were determined at 500 °C based on experimental results for 16 alloys. A ternary intermetallic compound (T1) in the palladium-rich region was confirmed by X-ray diffractometry. The experimental data were first compared with the results of a CALPHAD-type prediction, based on binary thermodynamic data using only a symmetrical Redlich?Kister?Muggianu model. In a second step, the thermodynamic modeling of the different phases in this ternary system was refined by including ternary interactions, and the phase diagram was calculated for the temperature range between 500 and 700 °C. With the optimized thermodynamic parameters the phase diagram was extrapolated to 200 °C and compared with preliminary experimental results.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BJ - Termodynamika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Intermetallics

ISSN

0966-9795

e-ISSN

—

Svazek periodika

15

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

8

Strana od-do

77-84

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—