Vliv orientace vzorku na creep kompozitu Mg- 10 obj. % Ti

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F07%3A00045443" target="_blank" >RIV/68081723:_____/07:00045443 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of Specimen Orientation on Creep of Mg?10 Vol. % Ti PM -Composite

Popis výsledku v původním jazyce

A magnesium matrix composite reinforced with 10 vol. % titanium particles with sizes below 0.025 mm was prepared through a powder metallurgical route with final hot extrusion at 400 °C. The specimens for compressive creep testing were machined from extruded bars of diameter 10 mm. The cylindrical specimens were cut in such a way that their axis and the axis of extruded bar contained a predestined angle from 0 to 90°. The stepwise loading at temperatures 300 and 350 °C was used. The technique enables todetermine the stress dependence of the creep rate. The dependence can be described by the Norton law with power greater than 20. The power is only slightly dependent on the specimen orientation. On the other hand, the creep rate at given applied stress is sensitive to the orientation: the greatest creep resistance is observed in specimens with axis parallel to the extrusion axis.

Název v anglickém jazyce

Influence of Specimen Orientation on Creep of Mg?10 Vol. % Ti PM -Composite

Popis výsledku anglicky

A magnesium matrix composite reinforced with 10 vol. % titanium particles with sizes below 0.025 mm was prepared through a powder metallurgical route with final hot extrusion at 400 °C. The specimens for compressive creep testing were machined from extruded bars of diameter 10 mm. The cylindrical specimens were cut in such a way that their axis and the axis of extruded bar contained a predestined angle from 0 to 90°. The stepwise loading at temperatures 300 and 350 °C was used. The technique enables todetermine the stress dependence of the creep rate. The dependence can be described by the Norton law with power greater than 20. The power is only slightly dependent on the specimen orientation. On the other hand, the creep rate at given applied stress is sensitive to the orientation: the greatest creep resistance is observed in specimens with axis parallel to the extrusion axis.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F06%2F1354" target="_blank" >GA106/06/1354: Vliv rozhraní matrice a zpevňující fáze na pevnost a tepelné vlastnosti kompozitů s matricí Mg-Al-Ca</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Magnesium: proceedings of the 7th International Conference on Magnesium Alloys and Their Application

ISBN

9783527317646

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

699-703

Název nakladatele

WILEY-VCH

Místo vydání

Weinheim

Místo konání akce

Dresden

Datum konání akce

6. 11. 2006

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—