Fatigue crack initiation in crystalline materials - experimental evidence and models

Popis výsledku v původním jazyce

Experimental evidence on the localization of the cyclic plastic strain and on the surface relief formation in cyclic loading of 316L austenitic stainless steel is presented. The focused ion beam is used for exposing three-dimensional evidence of persistent slip markings (PSMs). PSMs consist of extrusions and parallel or alternating intrusions which develop during cyclic loading. Monte Carlo simulations of vacancy generation within persistent slip band (PSB) and their migration to the matrix where they annihilate on the edge dislocations are used to simulate the growth of extrusions and intrusions. The results of the simulations are compared with experimental data and discussed in terms vacancy models of fatigue crack initiation.

Název v anglickém jazyce

Fatigue crack initiation in crystalline materials - experimental evidence and models

Popis výsledku anglicky

Experimental evidence on the localization of the cyclic plastic strain and on the surface relief formation in cyclic loading of 316L austenitic stainless steel is presented. The focused ion beam is used for exposing three-dimensional evidence of persistent slip markings (PSMs). PSMs consist of extrusions and parallel or alternating intrusions which develop during cyclic loading. Monte Carlo simulations of vacancy generation within persistent slip band (PSB) and their migration to the matrix where they annihilate on the edge dislocations are used to simulate the growth of extrusions and intrusions. The results of the simulations are compared with experimental data and discussed in terms vacancy models of fatigue crack initiation.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Key Engineering Materials

ISSN

1013-9826

e-ISSN

—

Svazek periodika

345-346

Číslo periodika v rámci svazku

-

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

4

Strana od-do

379-382

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—