Vliv nízké teploty na únavovou životnost a cyklickou deformační odezvu UFG mědi

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F07%3A00092321" target="_blank" >RIV/68081723:_____/07:00092321 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Effect of low temperature on fatigue life and cyclic stress-strain response of UFG copper
Popis výsledku v původním jazyce
Fatigue life curves and cyclic stress-strain curves of UFG copper were determined under stress control at room temperature and at a temperature of 173 K. At both the temperatures the lifetime of UFG cooper is longer than that of CG copper. The S-N curveof UFG copper is temperature dependent, while its cyclic stress-strain curve is temperature insensitive. Two mechanisms of cyclic plastic deformation in ultrafine-grained copper were proposed.
Název v anglickém jazyce
Effect of low temperature on fatigue life and cyclic stress-strain response of UFG copper
Popis výsledku anglicky
Fatigue life curves and cyclic stress-strain curves of UFG copper were determined under stress control at room temperature and at a temperature of 173 K. At both the temperatures the lifetime of UFG cooper is longer than that of CG copper. The S-N curveof UFG copper is temperature dependent, while its cyclic stress-strain curve is temperature insensitive. Two mechanisms of cyclic plastic deformation in ultrafine-grained copper were proposed.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—

Rok uplatnění
2007
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)