Kritéria iniciace trhlin ze singulárních koncentrátorů napětí. Část I: Obecné posouzení singulárních koncentrátorů napětí

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F07%3A00094876" target="_blank" >RIV/68081723:_____/07:00094876 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Crack initiation criteria for singular stress concentrations Part I: A universal assessment of singular stress concentrations

Popis výsledku v původním jazyce

In the contribution the limits of the validity of standard crack linear elastic fracture mechanics are extended to problems connected with failure of structures caused by general non-crack-like singular stress concentrators. In the present part of the contribution a universal approach to assessment of general singular stress concentrators in terms of linear elastic fracture mechanics is formulated. The approach suggested in this part of the paper facilitates the answer to the question whether or not a crack forms in the vicinity of the stress concentrator and what the parameters controlling crack initiation are. The presented approach follows the basic idea of linear elastic fracture mechanics, i.e. the validity of small scale yielding conditions is assumed, and has a phenomenological character.

Název v anglickém jazyce

Crack initiation criteria for singular stress concentrations Part I: A universal assessment of singular stress concentrations

Popis výsledku anglicky

In the contribution the limits of the validity of standard crack linear elastic fracture mechanics are extended to problems connected with failure of structures caused by general non-crack-like singular stress concentrators. In the present part of the contribution a universal approach to assessment of general singular stress concentrators in terms of linear elastic fracture mechanics is formulated. The approach suggested in this part of the paper facilitates the answer to the question whether or not a crack forms in the vicinity of the stress concentrator and what the parameters controlling crack initiation are. The presented approach follows the basic idea of linear elastic fracture mechanics, i.e. the validity of small scale yielding conditions is assumed, and has a phenomenological character.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Engineering Mechanics

ISSN

1802-1484

e-ISSN

—

Svazek periodika

14

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

10

Strana od-do

399-408

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—