Vliv mechanismu šíření trhliny na fraktální dimensi lomových ploch ocelí

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00099512" target="_blank" >RIV/68081723:_____/08:00099512 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27690/08:00019847

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

The effect of crack propagation mechanism on the fractal dimension of fracture surfaces in steels

Popis výsledku v původním jazyce

The paper reports on the results of a fractal analysis of fracture surfaces of Ni?Cr steel in two different states of heat treatment simulating embrittlement. The change in the fractal dimension of the fracture surface demonstrates a wavy character and dispersion depending on the microstructural state of the tested steel. The results of the fractal analysis in the crack growth direction and across the entire crack front were used as the basis for a reconstruction of the geometry of the fracture surface,providing a new geometric tool for fractographic analysis. The competing effects of transgranular and intergranular brittle fracture may lead to increased roughness of the fracture surface and its fractal dimension. The threshold value of the fractal dimension of the sections perpendicular to the fracture surface, indicating the transition from transgranular to intergranular fracture, is 1.12.

Název v anglickém jazyce

The effect of crack propagation mechanism on the fractal dimension of fracture surfaces in steels

Popis výsledku anglicky

The paper reports on the results of a fractal analysis of fracture surfaces of Ni?Cr steel in two different states of heat treatment simulating embrittlement. The change in the fractal dimension of the fracture surface demonstrates a wavy character and dispersion depending on the microstructural state of the tested steel. The results of the fractal analysis in the crack growth direction and across the entire crack front were used as the basis for a reconstruction of the geometry of the fracture surface,providing a new geometric tool for fractographic analysis. The competing effects of transgranular and intergranular brittle fracture may lead to increased roughness of the fracture surface and its fractal dimension. The threshold value of the fractal dimension of the sections perpendicular to the fracture surface, indicating the transition from transgranular to intergranular fracture, is 1.12.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Engineering Fracture Mechanics

ISSN

0013-7944

e-ISSN

—

Svazek periodika

75

Číslo periodika v rámci svazku

3-4

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

13

Strana od-do

726-738

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—