Difúze vodíku ve slitinách Mg-H a Mg-Ni-H

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00308977" target="_blank" >RIV/68081723:_____/08:00308977 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Hydrogen diffusion in Mg?H and Mg?Ni?H alloys

Popis výsledku v původním jazyce

Coefficients of hydrogen diffusion in Mg2NiH4 (DI), MgH2 (DM), and in (Mg + Mg2Ni)-H eutectic (DE) were measured in the temperature interval 449?723 K. Experimental material was prepared by two techniques: by melting and casting and by ball-milling and compacting into pellets. Hydrogen charging was carried out from the hydrogen gas phase at high temperature and pressure. The Mg2NiH4 pellets were prepared in different regimes resulting either in a structure with a high fraction or with a low fraction oftwinned low-temperature phase LT2. It was found that the LT2 slows down the hydrogen desorption rate considerably.

Název v anglickém jazyce

Hydrogen diffusion in Mg?H and Mg?Ni?H alloys

Popis výsledku anglicky

Coefficients of hydrogen diffusion in Mg2NiH4 (DI), MgH2 (DM), and in (Mg + Mg2Ni)-H eutectic (DE) were measured in the temperature interval 449?723 K. Experimental material was prepared by two techniques: by melting and casting and by ball-milling and compacting into pellets. Hydrogen charging was carried out from the hydrogen gas phase at high temperature and pressure. The Mg2NiH4 pellets were prepared in different regimes resulting either in a structure with a high fraction or with a low fraction oftwinned low-temperature phase LT2. It was found that the LT2 slows down the hydrogen desorption rate considerably.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BJ - Termodynamika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F07%2F0010" target="_blank" >GA106/07/0010: Difúze vodíku ve slitinách Mg-Ni modifikovaných vybranými prvky snižujícími stabilitu hydridů</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Materialia

ISSN

1359-6454

e-ISSN

—

Svazek periodika

56

Číslo periodika v rámci svazku

12

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

10

Strana od-do

—

Kód UT WoS článku

000257600900001

EID výsledku v databázi Scopus

—