Porovnání konvenčních a protlačovacích creepových zkoušek mechanicky legovaných slitin Al-C-O

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00310248" target="_blank" >RIV/68081723:_____/08:00310248 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Comparison of conventional and small punch creep tests of mechanically alloyed Al?C?O alloys

Popis výsledku v původním jazyce

Aluminum alloys reinforced by alumina and carbide particles were tested in small punch creep at temperatures of 623 and 723 K. The alloys were prepared by powder metallurgy route (mechanical alloying) and contained 0.8 wt.% of oxygen and 1 and 2 wt.% ofcarbon, respectively. The dependence of the time to fracture on the applied force closely resembles the stress dependence of the time to fracture in conventional tensile creep of the same alloys. The force in small punch test and the stress in conventional creep test of the same duration are thus linearly related. A new procedure for estimating the proportionality constant is presented. It is shown that the proportionality constant is dependent on the deflection observed at fracture in the small punch test.

Název v anglickém jazyce

Comparison of conventional and small punch creep tests of mechanically alloyed Al?C?O alloys

Popis výsledku anglicky

Aluminum alloys reinforced by alumina and carbide particles were tested in small punch creep at temperatures of 623 and 723 K. The alloys were prepared by powder metallurgy route (mechanical alloying) and contained 0.8 wt.% of oxygen and 1 and 2 wt.% ofcarbon, respectively. The dependence of the time to fracture on the applied force closely resembles the stress dependence of the time to fracture in conventional tensile creep of the same alloys. The force in small punch test and the stress in conventional creep test of the same duration are thus linearly related. A new procedure for estimating the proportionality constant is presented. It is shown that the proportionality constant is dependent on the deflection observed at fracture in the small punch test.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F02%2F0274" target="_blank" >GA106/02/0274: Protlačovací creepové zkoušky mechanicky legovaných hliníkových slitin</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Characterization

ISSN

1044-5803

e-ISSN

—

Svazek periodika

59

Číslo periodika v rámci svazku

7

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

000257053300019

EID výsledku v databázi Scopus

—